Karbon fiber katkılı poliamit 66 polimer kompozitlerin tribolojik özelliklerinin değerlendirilmesi

dc.authorid0000-0003-3065-6361en_US
dc.authorid0000-0002-6068-9204en_US
dc.authorid0000-0002-6224-3388en_US
dc.contributor.authorÖzsarıkaya, Bilal
dc.contributor.authorYetgin, Salih Hakan
dc.contributor.authorKöse, Sinan
dc.date.accessioned2023-12-27T08:23:26Z
dc.date.available2023-12-27T08:23:26Z
dc.date.issued2023en_US
dc.departmentİstanbul Ticaret Üniversitesien_US
dc.description.abstractBu çalışmada, poliamit 66 (PA66) polimeri ile ağırlık olarak % 10, %20 ve %30 oranlarında karbon elyaf (KE) takviyeli poliamit 66 kompozitlerinin aşınma ve sürtünme davranışları incelenmiştir. Aşınma deneyleri çelik diske karşı kuru ortam şartları altında gerçekleştirilmiştir. Karbon elyaf katkılı PA66 kompozitleri çift vidalı ekstruderde granül olarak üretilmiş sonrasında enjeksiyon makinesi ile aşınma test numuneleri basılmıştır. Aşınma testleri 0,4, 0,8 ve 1,2 m/s kayma hızlarında, 20, 30 ve 40N yükler altında yapılmıştır. Deneyler, ortam sıcaklığında pim-disk aşınma cihazında gerçekleştirilmiştir. 0,8 m/s hız ve 30N yükte, PA66 polimerine ilave edilen %10, %20 ve %30 oralarındaki KE, sürtünme katsayısını %12,4, %23,5 ve %32,7 oranında, aşınma oranlarını ise %19,9, %38,9 ve %82,0 oranında azaltmıştır. Artan yük ve hız ile sürtünme katsayısı ve aşınma oranı artmıştır. Genel olarak, PA66 ve PA66/KE kompozitlerin aşınma oranları 10-10 mm3 /Nm olarak elde edilmiştir. Aşınma oranı ve sürtünme katsayısı arasındaki korelasyon katsayısı (R2 ) PA66 polimeri için 0,9686, PA66/30KE kompozitin için ise 0,775 olarak elde edilmiştir. Uygulanan tribolojik test çalışma şartlarında % 30 oranında karbon elyaf takviyeli PA66 kompozitin katkısız PA66’ya göre ortalama %82 oranında dirençli olduğu belirlenmiştir.en_US
dc.description.abstractIn this study, the wear and friction performances of polyamide 66 (PA66) polymer and 10wt%, 20wt% and 30wt% carbon fibre (CF) reinforced polyamide 66 composites were investigated. Wear tests were carried out against a steel disc under dry ambient conditions. Carbon fibre reinforced PA66 composite was produced as granules in a twin screw extruder and then wear test specimens were molded in an injection molding machine. The wear tests were performed under 20-30-40N loads at sliding speeds of 0,4, 0,8 and 1,2 m/s. The tests were accomplished at ambient temperature using a pin-on-disc abrasion tester. At 0,8 m/s sliding speed and 30N load, 10%, 20% and 30% CF added to PA66 polymer reduced the coefficient of friction by 12,4%, 23,5% and 32,7%, and the wear rates by 19,9%, 38,9% and 82,0%. While the coefficient of friction and wear rate increased with the raise of the applied load and sliding speed. In general, the wear rates of PA66 and PA66/CF composites were obtained as 10-10 mm3 /Nm. The correlation coefficient (R2 ) between wear rate and friction coefficient was obtained as 0,9686 for PA66 polymer and 0,775 for PA66/30CF composite. In the tribological test working conditions applied, it was determined that carbon fibre reinforced PA66 with 30 % carbon fibre reinforcement was 82% resistant on average than PA66 polymer.en_US
dc.identifier.doi10.55071/ticaretfbd.1337774en_US
dc.identifier.endpage280en_US
dc.identifier.issue44en_US
dc.identifier.startpage267en_US
dc.identifier.urihttps://hdl.handle.net/11467/7063
dc.identifier.urihttps://doi.org/10.55071/ticaretfbd.1337774
dc.identifier.volume22en_US
dc.language.isotren_US
dc.publisherİstanbul Ticaret Üniversitesien_US
dc.relation.ispartofİstanbul Ticaret Üniversitesi Fen Bilimleri Dergisien_US
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Başka Kurum Yazarıen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectAşınma, karbon fiber, poliamit66, sürtünmeen_US
dc.subjectFriction, carbon fiber, polyamide66, wearen_US
dc.titleKarbon fiber katkılı poliamit 66 polimer kompozitlerin tribolojik özelliklerinin değerlendirilmesien_US
dc.title.alternativeEVALUATION OF TRIBOLOGICAL PROPERTIES OF CARBON FIBER FILLED POLYAMIDE 66 POLYMER COMPOSITESen_US
dc.typeArticleen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Yükleniyor...
Küçük Resim
İsim:
10.55071-ticaretfbd.1337774-3308465.pdf
Boyut:
1.15 MB
Biçim:
Adobe Portable Document Format
Açıklama:
Lisans paketi
Listeleniyor 1 - 1 / 1
Küçük Resim Yok
İsim:
license.txt
Boyut:
1.56 KB
Biçim:
Item-specific license agreed upon to submission
Açıklama: